利用等离子表面合金化技术在Ti6Al4V合金表面制备了钼-氮渗镀复合层, 通过调整氮氩流量比获得3种表面渗镀复合层, 对渗镀复合层的组织结构、显微硬度、耐腐蚀性能进行了研究。结果表明: 氮氩流量比影响合金表面渗镀复合层的组织结构、硬度; 渗镀复合层可明显提高Ti6Al4V合金在质量分数为37%沸腾盐酸溶液中的耐腐蚀性能; 随着氮氩流量比的增加, 复合层的厚度增加, 硬度提高, 耐腐蚀性能变差。

所属栏目

国家自然科学基金资助项目(50771070); 国家“863”科技支撑计划资助项目(2007AA03Z521)

收稿日期

2010/10/32011/7/6

作者单位

李咏梅:太原理工大学材料科学与工程学院, 太原 030024
张敏:太原理工大学表面工程研究所, 太原 030024
范爱兰:太原理工大学表面工程研究所, 太原 030024

备注

李咏梅(1970-), 女, 辽宁大连人, 高级工程师, 硕士。

引用该论文:

LI Yong-mei,ZHANG Ming,FAN Ai-lan.Preparation and Properties of Diffusion and Deposition Composite Layer of Mo-N on Ti6Al4V Alloy Surface[J].Materials for mechancial engineering,2011,35(10):1～3
李咏梅,张敏,范爱兰.Ti6Al4V合金表面钼-氮渗镀复合层的制备及性能[J].机械工程材料,2011,35(10):1～3

参考文献

【1】

SPROUL W D, GRAHAM M E, WONG M S,et al. Reactive unbalanced magnetron sputtering of the nitrides of Ti,Zr,Hf,Cr,Mo,Ti-Al, Ti-Zr and Ti-Al-V[J]. Surface and Coatings Technology,1993,61:139-143.

【2】

ANITHA V P, MAJOR S, CHANDRASHEKHARAM D,et al. Deposition of molybdenum nitride thin films by r.f. reactive magnetron sputtering[J]. Surface and Coatings Technology,1996,79:50-54.

【3】

DANROC J, AUBERT A, GILLET R.Hard molybdenum coatings prepared by cathodic magnetron sputtering[J]. Thin Solid Films,1987,153:281-286.

【4】

DONOVAN E P, HUBLER G K, MUDHOLKAR M S,et al. Ion-beam-assisted deposition of molybdenum nitride films[J]. Surface and Coatings Technology,1994,66:499-504.

【5】

WU J D, WU C Z, SONG Z M,et al. Preparation of molybdenum nitrides by laser-promoted nitridation reaction[J]. Thin Solid Films,1997,311:62-66.

【6】

AUBERT A, DANROCC J, GAUCHER A,et al. Hard chrome and molybdenum coatings produced by physical vapour deposition[J]. Thin Solid Films,1984,126:61-67.

【7】

URGEN M, ERYILMAZ O L, CAKIR A F,et al. Characterization of molybdenum nitride coatings produced by arc-PVD technique[J]. Surface and Coatings Technology,1997,94/95:501-506.

【8】

TANG B, WU P Q, LI X Y,et al. Tribological behavior of plasma Mo-N surface modified Ti-6Al-4V alloy[J]. Surface and Coatings Technology,2004,79:333-339.

【9】

TANG B, WU P Q, LI X Y,et al. Improventment of corrosion-wear resistance Ti-6Al-4V alloy by plasma Mo-N surface modification[J]. Advance Engineering Materials,2005,7(4):232-238.

【10】

李秀燕,范爱兰,唐宾,等.Ti6Al4V表面双层辉光离子渗Mo及其摩擦学性能的研究[J]. 摩擦学学报,2003,23(2):108-111.